|Curing Time:||4~8 Hours||Property:||Flow Automaticly|
|Product Name:||Self Leveling Floor Compound||Main Raw Material:||Sand|
|Hardening Feature:||Rapid Hardening||Type:||Modified Cement|
25kg Packing Self Leveling Floor Compound in Red Color
BES self leveling floor compound is made from elaborate aggregate of special cement and foreign polymer spraying dry resin and special additive, it’s nontoxic and environmental .It is the high strength& super fluidity self-leveling mix. It makes work easier with high fluidity, and it has perfect abrasion resistance with high strength.
-Portland cement based
-Provides a smooth surface
-Applications up to 10mm in a single pour
-Accepts non-moisture sensitive tile and stone in 24 hours
-Accepts floor covering sheet goods in 3 days
|Flowability (mm)||Initial flowability||≥135|
|Tensile adhesive strength (Mpa)||≥2.0|
|Wear resistance (g)||≤0.50|
|Dimensional change rate (%)||-0.15~+0.15|
|24h compressive strength (Mpa)||≥10|
|24h anti-bending strength (Mpa)||≥4.5|
|28 days compressive strength (Mpa)||≥4.5|
|28 days anti-bending strength (Mpa)||≥5|
1. The substrate must be clean, dry firm and no any residue, then use Xindadi special interface agent to paint the base plane.
2. After about 2-6 hours, mixed with water before construction, be sure to strictly self-leveling cement: water 25:6 ~ 6.5kg mixed. First 6 ~ 6.5kg of water into the bucket, then pour the product side down while stirring until a homogeneous mixture, lay up 1 minute, then stir once again briefly.
3. Pour the mixture into the construction area, a zigzag rake to move to a desired uniform thickness (thickness constructability 1-4mm).Before initial setting, use defoaming roller to exclude air which mixed in before.